Thin Slab SEN

/ladle

Optimized flow field design minimizes breakouts and surface defects, ensuring stable casting and improved slab surface quality.

Advanced nozzle geometry and flow control minimize clogging risk and maintain smooth molten steel flow throughout the casting process.

High-quality refractory compositions resist erosion, thermal stress, and steel penetration, extending nozzle lifespan and reducing downtime.

Ensures consistent molten steel delivery and reduces mold level fluctuations for improved casting stability and product uniformity.

SEN	Bowl		Body		Slag Line
Chemical Analysis	Range	Typical Value	Range	Typical Value	Range	Typical Value
SiO₂ (%)	--	13.18	--	24.72	--	3.59
TiO₂ (%)	--	1.15	--	0.56	--	0.24
Al₂O₃ (%)	--	1.32	65-71	68.52	--	0.65
Fe₂O₃ (%)	--	2.34	--	0.43	--	0.08
CaO (%)	--	1.05	--	0.27	--	2.54
MgO (%)	78-83	81.22	--	1.03	--	0.06
K₂O (%)	--	--	--	--	--	--
Na₂O (%)	--	--	--	--	--	--
B₂O₃ (%)	--	--	--	--	--	--
ZrO₂ (%)	--	0.85	--	3.77	91-95	93.01
Lgloss (%)	10-14	11.44	28-32	30.22	13-17	15.98
Cold Bending (Mpa)	4.5-8.5	6.75	7-14	12.3	5-10	8.6
Apparent Porosity (%)	11-17	15.22	11-17	12.8	11-18	13.5
Bulk Density (g/cm³)	2.65-2.80	2.72	2.45-2.65	2.55	3.65-3.85	3.78