/ladle
Anhydrous Tapping Clay
Time-Saving
No baking required. The fast-hardening property shortens furnace start-up time, significantly improving production efficiency.
High Performance
Exceptional resistance to high temperature and molten iron erosion effectively extends the service life of the tap hole.
Easy Operation
Convenient to use, easy to control, and reduces operational complexity during furnace tapping.
|
Brand
|
ZTM-PN1
|
ZTM-2PN
|
ZTM-PN3
|
ZTM-PN4
|
|
|---|---|---|---|---|---|
|
Chemical Composition (%)
|
Al₂O₃
|
≥20
|
≥25
|
≥30
|
≥30
|
|
SiC+C
|
≥35
|
≥30
|
≥25
|
≥25
|
|
|
Normal Temperature
Withstand Voltage (mpa)
|
1450℃×3h (Buried Charcoal)
|
≥10
|
≥15
|
≥20
|
≥25
|
|
Apparent Porosity (%)
|
≤28
|
≤28
|
≤25
|
≤25
|
|
|
Volume Density (g/cm⁻³)
|
≥1.8
|
≥1.9
|
≥2.0
|
≥2.1
|
|
|
Liner Rate of Change
After Burnt (%)
|
+1～-0.5
|
+0.5～0
|
+0.5～0
|
+0.5～0
|
|
|
Binder Type
|
Environmental
Bonding Agent
|
Environmentally Friendly Binder & Resin
|
Environmentally Friendly Binder & Resin
|
Environmentally Friendly Binder & Resin
|
|
|
Scope of Application
|
Blast Furnace Below 1000m³
|
1000~1800m³
Blast Furnace
|
18f0~2800m³
Blast Furnace
|
Blast Furnace
above 3000m³
|
|
Partner with lnzc
Our experts are ready to help you identify the best Anhydrous Tapping Clay solution for your process.
Customized Anhydrous Tapping Clay Solutions
Formulation Customized
Adjusted according to blast furnace operating temperature and process requirements to achieve optimal heat resistance.
Flowability Customization
Formulated to match customer equipment and operating habits for smooth and efficient tapping.
Strength Customization
Tuned based on tapping pressure and frequency to ensure stability and durability.
Hardening Speed Customization
Controlled according to tapping rhythm and production schedule to maximize efficiency.