/ladle
Al₂O₃-SiC Castable
Excellent Erosion Resistance
Effectively withstands attack from molten iron, slag, and corrosive gases, extending lining service life.
Strong Anti-Penetration
Optimized particle size distribution forms a dense structure, preventing molten iron penetration and reducing structural damage.
Easy Application
Simple mixing and construction process, suitable for both casting and gunning applications.
|
Brand
|
ZTM-TBJ-L60
|
ZTM-TBJ-L65
|
ZTM-TBJ-L70
|
|---|---|---|---|
|
Al₂O₃ (%)
|
≥60
|
≥65
|
≥70
|
|
SiC (%)
|
≥8
|
≥8
|
≥8
|
|
Bulk Density (g.cm⁻³)
|
≥2.40
|
≥2.50
|
≥2.65
|
|
Cold Crushing Strength (MPa)
|
≥20 (110℃, 24h)
|
≥25 (110℃, 24h)
|
≥30 (110℃, 24h)
|
|
≥30 (1000℃, 3h)
|
≥35 (1000℃, 3h)
|
≥40 (1000℃, 3h)
|
|
|
±0.5 (1400℃, 3h)
|
±0.5 (1400℃, 3h)
|
±0.4 (1400℃, 3h)
|
|
|
Applicantion
|
Iron Ladle
|
Iron Ladle with Desulphurizating Pretreatment
|
|
Partner with lnzc
Our experts are ready to help you identify the best Al₂O₃-SiC Castable solution for your process.
Customized Al₂O₃-SiC Castable Solutions
Formulation Customized
Tailored to molten iron composition, slag characteristics, and working environment for optimal performance.
Particle Size Optimization
Improved grading design for higher density, strength, and erosion resistance.