Al₂O₃-SiC-C Brick
Excellent Corrosion Resistance
Effectively resists erosion from molten iron and slag, extending lining life and maintaining structural integrity.
Thermal Shock Resistance
Resists rapid temperature changes to prevent cracking and spalling, ensuring operational stability.
High Strength & Abrasion Resistance
Withstands hot metal impact and mechanical wear, providing enhanced durability and reduced maintenance frequency.
|
Brand
|
ZTM-ASC-L14
|
ZTM-ASC-L16
|
ZTM-ASC-L18
|
ZTM-ASC-L18B
|
|---|---|---|---|---|
|
Al₂O₃ (%)
|
≥55
|
≥60
|
≥60
|
≥65
|
|
SiC+C (%)
|
≥14
|
≥16
|
≥18
|
≥18
|
|
Bulk Density (g.cm⁻³)
|
≥2.55 (200℃, 24h)
|
≥2.60 (200℃, 24h)
|
≥2.65 (200℃, 24h)
|
≥2.75 (200℃, 24h)
|
|
Apparent Porosity (%)
|
≤10 (200℃, 24h)
|
≤10 (200℃, 24h)
|
≤8 (200℃, 24h)
|
≤8 (200℃, 24h)
|
|
Crushing Strength (MPa)
|
≥40 (200℃, 24h）
|
≥35 (200℃, 24h）
|
≥35 (200℃, 24h）
|
≥35 (200℃, 24h）
|
|
Permanent Linear Change (%)
|
0～+1.0 (1400℃, 3h)
|
0～+1.0 (1400℃, 3h)
|
0～+1.0 (1400℃, 3h)
|
0～+1.0 (1400℃, 3h)
|
|
Applicantion
|
Side Wall
|
Side Wall
|
Slag Line, Bottom
|
Slag Line, Bottom
|
Partner with lnzc
Our experts are ready to help you identify the best Al₂O₃-SiC-C Brick solution for your process.
Customized Al₂O₃-SiC-C Brick Solutions
Formulation Customized
Tailored to molten iron composition, slag characteristics, and service temperature for optimal corrosion resistance.
Size Customization
Brick sizes and shapes precisely designed to fit specific iron ladle geometries and operating conditions.