/ladle
AL₂O₃-SiC-C Brick
Excellent Slag Resistance
Effectively resists chemical attack and penetration from molten iron and slag, ensuring lining integrity.
High Wear Resistance
Withstands erosion from hot gases and molten iron flow, significantly reducing lining loss.
Thermal Shock Resistance
Maintains structural stability under frequent temperature fluctuations, minimizing cracking and spalling.
|
Brand
|
ZTM-ASC-T18A
|
ZTM-ASC-T18B
|
ZTM-ASC-T20A
|
ZTM-ASC-T20B
|
|---|---|---|---|---|
|
Al₂O₃ (%)
|
≥65
|
≥65
|
≥65
|
≥60
|
|
SiC+C (%)
|
≥18
|
≥18
|
≥20
|
≥20
|
|
Bulk Density (g.cm⁻³)
|
≥2.85 (200℃, 24h)
|
≥2.75 (200℃, 24h)
|
≥2.85 (200℃, 24h)
|
≥2.80 (200℃, 24h)
|
|
Apparent Porosity (%)
|
≤10 (200℃, 24h)
|
≤10 (200℃, 24h)
|
≤10 (200℃, 24h)
|
≤10 (200℃, 24h)
|
|
Cold Crushing Strength (MPa)
|
≥50 (200℃, 24h)
|
≥40 (200℃, 24h)
|
≥40 (200℃, 24h)
|
≥40 (200℃, 24h)
|
|
Permanent Linear Change (%)
|
0～+1.0 (1400℃, 3h)
|
0～+1.0 (1400℃, 3h)
|
0～+1.0 (1400℃, 3h)
|
0～+1.0 (1400℃, 3h)
|
|
Applicantion
|
Side Wall
|
Top
|
Impact Area
|
Slag Line
|
Partner with lnzc
Our experts are ready to help you identify the best AL₂O₃-SiC-C Brick solution for your process.
Customized AL₂O₃-SiC-C Brick Solutions
Formulation Customized
Tailored compositions based on hot metal chemistry, slag characteristics, and operating temperature for optimal performance.
Size Customization
Brick sizes and shapes designed to precisely fit torpedo car geometry and lining configurations.