/ladle
MgO-C Brick
Superior Corrosion Resistance
Exceptional resistance to slag, gas, and high-temperature erosion minimizes wear and extends the lining service life.
Enhanced Steel Quality
Low impurity release minimizes contamination from refractories, ensuring cleaner molten steel and higher-quality output.
High Mechanical Strength & Toughness
Withstands molten steel impact, scrap abrasion, and thermal stress to ensure long-term durability and operational safety.
|
Brand
|
ZTM-ZMT-10
|
ZTM-ZMT-12
|
ZTM-ZMT-14
|
ZTM-ZMT-16
|
ZTM-ZMT-18
|
|---|---|---|---|---|---|
|
MgO (%)
|
≥80
|
≥78
|
≥76
|
≥74
|
≥72
|
|
C (%)
|
10
|
12
|
14
|
16
|
18
|
|
Apparent Porosity (%)
|
≤3.0
|
≤3.0
|
≤3.0
|
≤3.0
|
≤3.0
|
|
Bulk Density (g.cm⁻³)
|
≥3.10
|
≥3.10
|
≥3.03
|
≥3.00
|
≥2.97
|
|
Cold Crushing Strength (MPa)
|
≥40
|
≥40
|
≥40
|
≥35
|
≥35
|
|
HMOR (MPa) (1450℃, 30min)
|
≥8
|
≥8
|
≥10
|
≥10
|
≥10
|
|
Applicantion
|
The Sidewall and Bottom of Ladle Working Lining for Normal Carbon Steel Production.
|
Used for the trunnion, tapping and molten pool.
|
|||
Partner with lnzc
Our experts are ready to help you identify the best MgO-C Brick solution for your process.
Customized MgO-C Brick Solutions
Formulation Customized
Tailored compositions based on slag chemistry, steel grade, and process parameters to achieve optimal corrosion resistance and stability.
Size Customization
Precise dimensions engineered to match ladle bottom geometry and operational conditions.
Technical Support
Professional guidance from design optimization to on-site application, ensuring best performance in service.